Thread: Stick welding issues
-
9th Sep 2021, 06:13 PM #1
Stick welding issues
Hi guys, I'm a backyard operator trying to master stick welding RHS , looking for a nice consistent quality looking weld using my Bossweld 180amp welder on rhs tube 2-3mm , straight single run beads looks fine , but as soon as i join two pieces same material together and run the same bead it eventually blows holes usually at the end or ends up looking terrible with worm holes and porosity ??? I'm running the welder at 135 + amps for a smooth finish using 3.2mm 6013 Stonebridge rods. I've noticed running any lower than 110 amps the welds are full of worm holes and porosity ? This issue is doing my head in. btw i can get satisfactory results using my mig gas welder on same material but i prefer stick. Pics below.
what are your thoughts on fixing the problem ? i'm sorta leaning towards getting a new welder , also thinking of changing rods to 6010, 6011 ,7010 ,7018 , 7024 and see which rod works better than 6013.
Cheers
-
9th Sep 2021, 06:45 PM #2
Hi Iron triangle,
Welcome to the MetalWork Forums.
To help you explore the other areas of our forum here's a guide on to to navigate our Forum and find all the interesting places.
Goto the FORUM box in the top left hand cnr of the page and click the down arrow. This will bring up a pull down menu that has Forum Home at the top
Click Forum Home which will present a scroll down page.
Our rules,the Terms of Service are right at the top ,we encourage you to read them.
Below that are all the various areas and sub forums that make up out MetalWork forums.
Welcome
Grahame
-
9th Sep 2021, 06:48 PM #3Most Valued Member
- Join Date
- Aug 2011
- Location
- Melbourne
- Posts
- 4,779
Hi there,
I'm not a qualified welder, just a backyard hack.
3.2mm rods are too big for that RHS. Try using 2.5mm rods. Then you should be able to turn the current down to maybe 85 amps. This will be more forgiving.
Also I find that when joining two pieces of RHS, placing 2-3 spot tacks prior to welding a seam will help absorb the heat and less likely to burn a hole when welding a bead.
Simon
Sent from my SM-G970F using TapatalkGirl, I don't wanna know about your mild-mannered alter ego or anything like that." I mean, you tell me you're, uh, super-mega-ultra-lightning babe? That's all right with me. I'm good. I'm good.
-
9th Sep 2021, 07:00 PM #4Pink 10EE owner
- Join Date
- Aug 2008
- Location
- near Rockhampton
- Posts
- 6,218
Looks to me like the first photo weld was done with a MIG.
Gold, the colour of choice for the discerning person.
-
9th Sep 2021, 07:10 PM #5
If you buy electrodes,buy 6012. Buy them in 2.6mm diameter.
Make sure to run them on electrode negative.
Dispensing with the welder terms what is happening you have too much ( 3.2mm) electrode trying to fill a much smaller area than the fillet.
Add to this the 6013s has a thin flux which does not allow the metal cooling from molten to solid as quickly. Weld bead will cool down fast when it is supported by the thicker 6012 flux, so less liable to burn a hole.
You are tying to butt weld an open edge-the cut edge to the rolled edge. With 130 amps the thin edge will burn away before it can pick up the rolled edge side.
When the arc is dropping molten metal in the joint the thin cut edge cannot dissipate heat quickly enough and wants to burn away.
With a 3.2mm diameter electrode you are stuck with high amps but can't go quick enough to avoid burn through /partial burn through.
Time to cheat a bit. Build up the rolled edge -the non cut side with short runs- and dip to cool the metal after each run. Flush off the metal with a disc to form a nice square edge which will butt up nicely to the other edge-the cut edge. tack corners and use the 6012 at very short arc.
If both tubes are to be welded at cut edges make sure they are cut square and tack each corner with no gaps.
Incline the area to be welded ( maybe 20 degrees) and run quickly downhill from tack to tack. Let cool and flip over and weld opposite side. Other two faces -exactly the same method.
Grahame
-
9th Sep 2021, 07:23 PM #6
-
9th Sep 2021, 07:50 PM #7Diamond Member
- Join Date
- Sep 2006
- Location
- Mallacoota,VIC,Australia
- Age
- 53
- Posts
- 1,010
I looked up Stone Bridge Electrodes and they are made in China. I have used two different brands of Chinese rods about 30 years ago, one brand worked well and the other brand well your second picture is a reminder of them - they just wouldn't weld properly. Also you say your using 3.2mm rods at 135 amps, as far as I know 130 amps is the maximum amps for a 3.2mm general purpose rod so for starters you have the electrode maxed out in term of amps. As others have said get some 2.5 or 2.6mm electrodes and try and get a better brand such as Gemini, Lincoln, Wia, Cigweld and have another try. I would be starting at about 70 amps and adjusting as necessary.
All The Best steran50 Stewart
The shortest way to do many things is to do only one thing at once.
-
11th Sep 2021, 11:52 AM #8
Thanks for all the tips guys much appreciated , i pickup some brand name 2.6mm rods today and had more success but not all the time , i'd get 3 sides looking ok but the last side had same probs. A couple of things i noticed , the beads looked better when the rod is angled at 70 degrees rather than 30, and doing a second and 3rd pass at more amps helped fixed the first and 2nd pass. I'm gonna have to say that my cheap welder is the problem and cannot do what i want it too because it simply cannot be that hard to run a smooth weld joint on 2.5mm rhs. I'm gonna go welding store and ask if i can test drive a few machines and see what happens.
-
11th Sep 2021, 12:08 PM #9Member: Blue and white apron brigade
- Join Date
- Feb 2006
- Location
- Perth
- Posts
- 7,189
It looks like you just need bit more practice.
I reckon you will learn a lot more by persisting in trying to improve your technique rather than jumping to immediately blaming the welder.
FWIW no amount of Youtube, or information on these forums, is going to beat a hour or so's tutorial with an experienced welder.
Finished beads are limited in providing feedback the welder needs to watch you welding and correct your technique.
My boiler maker BIL with 40+ years of welding experience showed me how to run decent beads with my $99 bunnings welder in about an hour. Then after a couple of months of practice he loaned me his $999 welder and the improvement was marginal at best.
Welding has similarities to making espresso, it's "mano, machina, materiale" - operator, machinery and materials - ie machinery is just one of 3 critical aspects
-
11th Sep 2021, 05:31 PM #10Pink 10EE owner
- Join Date
- Aug 2008
- Location
- near Rockhampton
- Posts
- 6,218
Stick welding and MIG welding are nothing alike. If you are fair at stick welding then it is easy to migrate to MIG. If you are fair at MIG welding, your stick welds will be really crappy.
I would be under average for stick welding skills, but managed this with cheap $7/5kg rods and a sub $100 ebay inverter welder that I can not kill despite trying with 4mm rods .Gold, the colour of choice for the discerning person.
-
12th Sep 2021, 04:08 AM #11China
- Join Date
- Dec 2005
- Location
- South Australia
- Posts
- 1,658
Am I missing something here, you have a MIG welder and you produce what look like quality welds, you are not Au fait with stick welding so your welds are rubbish, and you blame the machine
Why not just use the MIG
-
12th Sep 2021, 08:14 PM #12
Similar Threads
-
Lets have your stick welding tip.
By Grahame Collins in forum WELDINGReplies: 30Last Post: 25th Mar 2018, 10:11 AM -
Help a beginner - stick welding
By mhewitt in forum WELDINGReplies: 16Last Post: 1st Jul 2013, 05:51 PM -
old stick welding m/c
By gpigeon in forum WELDINGReplies: 24Last Post: 27th Mar 2012, 07:06 AM -
Stick welding polarity
By Corgan in forum WELDINGReplies: 1Last Post: 1st Aug 2011, 09:28 PM -
Stick Welding
By Grahame Collins in forum WELDINGReplies: 51Last Post: 17th Sep 2007, 11:10 AM